Pt Effect on the Bond-Coating/Superalloy Interdiffusion: Case of a Pt-Modified NiCoCrAlYTa Coating

Overview & Synopsis

Heat treatments and oxidation tests were performed on systems composed of a single-crystal AM3 superalloy with a NiCoCrAlYTa+Pt coating to investigate the effect of Pt on Ta and Ti diffusion at high temperature. Experimental results were compared to an AM3 superalloy directly coated with Pt. For all the studied systems, the effect of Pt on elemental activities was evaluated through thermodynamic calculations. Pt diffusion was found to be faster in the NiCoCrAlYTa coating than in AM3. High Ta contents were measured in the Pt-rich γ ′ phase below the surface and significant Al and Cr transport toward the surface was observed, in agreement with thermodynamic calculations which predicted an important decrease in their activities in the presence of Pt. An outward diffusion of Ti was also noticed, whereas calculations did not show a decrease in Ti activity due to Pt. Other discrepancies between experiments and thermodynamic calculations were noted and are discussed in this work.