Effect of Solid/Liquid and Eutectic Front Velocities on Microstructure Evolution in Al-20%Cu Alloys

During the solidification process, microstructures are affected by the experimental conditions, the thermophysical characteristics of the alloy, and the type of grain-refining particles. Unidirectional solidification experiments were performed in a vertical Bridgman-type furnace to investigate the effect of the solidification front velocity on the solidified microstructure of a non-refined and refined Al-20%Cu alloy. The samples were solidified by rapidly increasing the sample velocity (v) range from 0.02 mm/s to 0.2 mm/s while maintaining an almost constant temperature gradient (~5 K/mm). As a result, despite changes in the solid/liquid front velocity along the sample, the microstructure of the non-refined alloys remained columnar. In the refined alloy, the columnar structure changed into an equiaxed structure at two different front velocities.

# Crystallography # Al-20%Cu # columnar-to-equiaxed transition (CET) # grain refinement # unidirectional solidification # Bridgman-type furnace

Alaaldeen Abdallah, András Roósz, Arnold Rónaföldi, et al. (2024). "Effect of Solid/Liquid and Eutectic Front Velocities on Microstructure Evolution in Al-20%Cu Alloys". Crystals. https://doi.org/10.3390/cryst14070638